0.05mm Fecral Resistance Heating Strip For Catalytic Converter

Product Categories
Shanghai Tankii Alloy Material Co.,Ltd
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment
Contact Now

0.05mm Fecral Resistance Heating Strip For Catalytic Converter

Brand Name : TANKII

Model Number : X8cral 20-6

Certification : ISO9001

Place of Origin : Shanghai

MOQ : 50kg

Payment Terms : L/C, T/T, Western Union

Supply Ability : 90+ton+per month

Delivery Time : 8-15 days

Packaging Details : to wind with thin film, bubble film,carton,wooden pallet or case

material : fecral

condition : soft annealed

surface : bright

shape : foil,strip,sheet

Contact Now

X8cral 20-6 fecral alloy Catalytic Converter Foil for Heat Element

Fecral alloy is high resistance and electrical heating alloy. Fecral alloy can reach process temperature of 2192 to 2282 F, corresponding to oa resistance temperature of 2372 F.

It is normally used in electrical furnace, glass top hobs, quartz tube heaters, resistors, catalytic converter,heating elements etc.

Nominal Analysis

21.00 Cr, 6.00 Al, Bal. Fe

Max contineous working temperature: 1250º C.

Melting Temperature: 1500º C

Thickness 0.05~0.1mm, width 1-1000mm

Usage: Catalytic converters

Material 1.4767, DIN 17470

Brand name 1Cr13Al4 0Cr25Al5 0Cr21Al6 0Cr23Al5 0Cr21Al4 0Cr21Al6Nb 0Cr27Al7Mo2
Main chemical composition% Cr 12.0-15.0 23.0-26.0 19.0-22.0 22.5-24.5 18.0-21.0 21.0-23.0 26.5-27.8
Al 4.0-6.0 4.5-6.5 5.0-7.0 4.2-5.0 3.0-4.2 5.0-7.0 6.0-7.0
RE opportune
amount		 opportune
amount		 opportune
amount		 opportune
amount		 opportune
amount		 opportune
amount		 opportune
amount
Fe Rest Rest Rest Rest Rest Rest Rest
Nb0.5 Mo1.8-2.2
Max.continuous
service temp.of
element (ºC)		 950 1250 1250 1250 1100 1350 1400
Resistivity
μΩ.m,20ºC		 1.25 1.42 1.42 1.35 1.23 1.45 1.53
Density
(g/cm3 )		 7.4 7.10 7.16 7.25 7.35 7.10 7.10
Thermal
conductivity
KJ/m.h.ºC		 52.7 46.1 63.2 60.2 46.9 46.1 45.2
Coefficient of
lines expansion
α×10-6/ºC		 15.4 16.0 14.7 15.0 13.5 16.0 16.0
Melting pointºC 1450 1500 1500 1500 1500 1510 1520
Tensile strength
Mpa		 580-680 630-780 630-780 630-780 600-700 650-800 680-830
Elongation at
rupture %		 >16 >12 >12 >12 >12 >12 >10
Variation of
area %		 65-75 60-75 65-75 65-75 65-75 65-75 65-75
Repeat bending
frequency(F/R)		 >5 >5 >5 >5 >5 >5 >5
Hardness(H.B.) 200-260 200-260 200-260 200-260 200-260 200-260 200-260
Micrographic
structure		 Ferrite Ferrite Ferrite Ferrite Ferrite Ferrite Ferrite
Magnetic
properties		 Magnetic Magnetic Magnetic Magnetic Magnetic Magnetic Magnetic


0.05mm Fecral Resistance Heating Strip For Catalytic Converter0.05mm Fecral Resistance Heating Strip For Catalytic Converter0.05mm Fecral Resistance Heating Strip For Catalytic Converter0.05mm Fecral Resistance Heating Strip For Catalytic Converter0.05mm Fecral Resistance Heating Strip For Catalytic Converter0.05mm Fecral Resistance Heating Strip For Catalytic Converter0.05mm Fecral Resistance Heating Strip For Catalytic Converter


Product Tags:

Fecral Resistance Heating Strip

      

Catalytic Converter Resistance Heating Strip

      

0.05mm Resistance Heating Strip

      
Quality 0.05mm Fecral Resistance Heating Strip For Catalytic Converter for sale

0.05mm Fecral Resistance Heating Strip For Catalytic Converter Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Shanghai Tankii Alloy Material Co.,Ltd
*Subject:
*Message:
Characters Remaining: (0/3000)
 
You May Like